FINISOL® GEL A+B
Transparent two-component solvent-based polyurethane gel (a+b)
Solvent-based two-component polyurethane gel. Transparent protective finish for decorative stone carpet and resinous surfaces.
Excellent resistance to yellowing. Glossy appearance.
Type: Polyurethane Solvent Top-Coatings
Description
Transparent gel based on aliphatic polyurethane resins.
FINISOL GEL forms a film that maintains good flexibility and good resistance to abrasion and scratching.
It resists ultraviolet rays thanks to UV filters that prevent photo-oxidative degradation.
Glossy appearance.
Use
To Coating for resinous covering such decorative grit or SIVIT STONE PU
Support
The substrate should not be wet or inconsistent.
Preparation of the support
Remove any remaining dust. Remove any loose or protruding pebbles.
Resin covering must be sanded or grinded, thus eliminating dust residues. In the case of new resin coatings, it is necessary to check the overcoating of the previously applied product.
Application
Combine the two components (A+B) and mix with a mixing drill for 1 minute.
Apply the mixture with a resin roller with a consumption of about 0.300 kg/m2.
To obtain a rough and non-slip surface, 5% of SFERETTE DI VETRO GRANDI or 10% of QUARZO RESINATO B0/B1 must be added in the 2 components.
Avoid preparing partial mixtures of product so as not to incur accidental errors, which could lead to failure or complete hardening.
Technical specifications
| PRODUCT DATA | |
|---|---|
| Color | Transparent |
| Consumption | about 0.300 kg/m2 |
| Specific weight (at 25°C) | mixture (A+B): circa 1,00 kg/ml |
| Viscosity (at 25°C) | mixture (A+B): 1200-1300 mPa.s |
| Ready-to-use VOC (Legislative Decree 161/06) | < 500 g/l Cat.A/j. Two-component, high-performance (BS) paint. |
| Solvent for tool cleaning | UNI Solvent |
| Storage | 12 months, store in a dry place at a temperature between 5°C and 30°C; pay particular attention to component B, which is sensitive to humidity |
| APPLICATION DATA AND TIMES | |
|---|---|
| Mixture Ratio | Weight : A=100, B=27 |
| Pot-life (50% U.R.) | at 25°C 90 min at 35°C 40 min |
| Dry to the touch (50% R.H.) | at 25°C 8-10 hours at 35°C 5-7 hours |
| Walkable (50% U.R.) | at 25°C 12-24 hours |
| Trafficable (50% R.H.) | 3-5 days |
| Deep hardening (50% R.H.) | at 25°C 7 days |
| Environmental conditions of use | Temperatures between +10°C and +35°C |
| TECHNICAL PERFORMANCE DATA | |
|---|---|
| Aspect | Glossy |